This specifications covers one type of manganesemolybdenum and four types of manganese-molybdenumnickel alloy steel plates for use in the quenched and tempered condition for the construction of welded pressure vessels. Material under this specification is available in five types, designated “A”, “B”, “C”, “D”, and “E”. The material is also available in three classes having the following strength levels.The maximum thickness of Class 1 and Class 2 plates is limited only by the capacity of the composition to meet the specified mechanical property requirements; however, current practice normally limits the maximum thickness to 12 in. [300 mm] for Types A through D. Current practice limits the maximum thickness for Type E to 6 in. [150 mm] for Class 1 and 31⁄4 in. [80 mm] for Class 2.
Grades | Description |
---|---|
Type A | - |
Type B | - |
Type C | - |
Type D | - |
Type E | - |
Type | Carbon, maxA | Manganese B | Phosphorus,maxA | Sulfur,maxA | Silicon | Molybdenum | Nickel | Chromium, max |
---|---|---|---|---|---|---|---|---|
Type A | 0.25 | 1.07–1.62 | 0.025 | 0.025 | 0.13–0.45 | 0.41–0.64 | - | - |
Type B | 0.25 | 1.07–1.62 | 0.025 | 0.025 | 0.13–0.45 | 0.41–0.64 | 0.37–0.73 | - |
Type C | 0.25 | 1.07–1.62 | 0.025 | 0.025 | 0.13–0.45 | 0.41–0.64 | 0.67–1.03 | - |
Type D | 0.25 | 1.07–1.62 | 0.025 | 0.025 | 0.13–0.45 | 0.41–0.64 | 0.17–0.43 | - |
Type E | 0.25 | 1.04–1.84 | 0.020 | 0.015 | 0.13–0.45 | 0.21–0.64 | 0.57–1.03 | 0.64 |
Class |
Tensile strength,min: ksi [MPa] |
Yield strength,min: ksi [MPa] |
Elongation in 2 in. [50 mm] min, %A |
---|---|---|---|
Class 1 | 80–100 [550–690] | 50 [345] | 18 |
Class 2 | 90–115 [620–795] | 70 [485] | 16 |
Class 3 | 100–125 [690–860] | 83 [570] | 16 |