ASTM A193 Grade B8PA Specification for high tensile bolts, screws, stud bolts, anchor bolts, threaded rods and other externally threaded fasteners, made from 305 stainless steel.

ASTM A193 Grade B8PA is a standard material specification for corrosion resistant austenitic stainless steel fasteners, for use in high tensile, high temperature and special purpose applications such as pressure piping & pressure vessels bolting. Grade B8PA is a heat-treated, work-hardened (or both) austenitic stainless steel further divided into class 1, class 1D & class 2, each having a distinguished tensile strength. This specification covers requirements for chemical composition, mechanical properties, hardness, heat-treatment and recommended nuts-washers for Grade B8PA Fasteners.

Tensile Class

Property	Description
Class 1	Carbide Solution Treated
Class 1D	Carbide Solution Treated
Class 2	Carbide Solution Treated & Strain Hardened

Chemical Composition

Element	Austenitic Stainless Steel
	AISI 305 / UNS S30500 / 1.4303
	CompositionA, %
Carbon	0.12 max
Manganese	2.00
Phosphorus	0.045 max
Sulfur	0.030 max
Silicon	1.00 max
Chromium	17.00 - 19.00
Nickel	11.00 - 13.00

^AThe intentional addition of Bi, Se, Te, and Pb is not permitted.

Mechanical Properties

Tensile Class	Diameter, Inch	Tensile Strength, min, ksi	Yield Strength, min, 0.2% offset, ksi	Elongation in 4D, min, %	Reduction of Area, min, %	Hardness, max
								Class 1 & 1DA	All Sizes	75	30	30	50	223 HBW or 96 HRBB
						Class 2C	3/4 and under	125	100	12	35	321 HBW or 35 HRCD
over 3/4 to 1 inclusive	115	80	15	35
over 1 to 1-1/4 inclusive	105	65	20	35
over 1-1/4 to 1-1/2 inclusive	100	50	28	50

A: Carbide Solution Treated
B: For sizes 3⁄4 in. in diameter and smaller, a maximum hardness of 241 HBW (100 HRB) is permitted.
C: Carbide Solution Treated and Strain Hardened
D: For diameters 11⁄2 and over, center (core) properties may be lower than indicated by test reports which are based on values determined at 1⁄2 radius.